PA66 INVISTA™ G3000HR BK34
47
- Properties:Filler: Glass fiber reinfGood dimensional stabilitHigh tensile strengthHydrolysis resistancethermal stabilityGood demolding performanc30% filler by weight
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ISO 294-4 | 0.95-1.05 % | |
| ISO 294-4 | 0.30-0.40 % | ||
| Water absorption rate | ISO 62 | 1.2 % | |
| ISO 62 | 1.8 % | ||
| Shrinkage rate | ISO294-4 | 0.95to1.1 % | |
| ISO294-4 | 0.30to0.40 % | ||
| Water absorption rate | ISO62 | 1.2 % | |
| ISO62 | 1.8 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527 | 9800 Mpa | |
| tensile breaking strength | ISO 527 | 195 Mpa | |
| Elongation | ISO 527 | 3.1 % | |
| Flexural modulus | ISO 178 | 9100 Mpa | |
| bending strength | ISO 178 | 270 Mpa | |
| Charpy Notched Impact Strength | ISO 179 | 9.0 kJ/m² | |
| ISO 179 | 10 kJ/m² | ||
| Impact strength of cantilever beam gap | ISO 180 | 10 kJ/m² | |
| Tensile modulus | ISO527-2 | 9800 Mpa | |
| Tensile stress | ISO527-2 | 195 Mpa | |
| Tensile strain | ISO527-2 | 3.1 % | |
| Flexural modulus | ISO178 | 9100 Mpa | |
| Bending stress | ISO178 | 270 Mpa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ISO 75 | 255 °C | ||
| ISO 75 | 248 °C | ||
| Melting temperature | ISO 11357 | 262 °C | |
| ISO75-2/B | 255 °C | ||
| ISO75-2/A | 248 °C | ||
| melting temperature | ISO11357-3 | 262 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.