ABS+PET Starex GC-0700 H LOTTE KOREA
0
CompareTechnical Data Sheet
| 物理性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 密度 | ISO1183 | 1.09 g/cm³ | |
| 熔体质量流动速率 | 250°C/10.0kg | ASTMD1238 | 40 g/10min |
| 250°C/10.0kg | ISO1133 | 40 g/10min | |
| 收缩率 | MD：3.20mm | ASTMD955 | 0.40to0.70 % |
| 密度 | ASTMD792 | 1.09 g/cm³ |
| 机械性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 拉伸模量 | ASTMD638 | 1800 MPa | |
| ISO527-2/50 | 2000 MPa | ||
| 抗张强度 | Yield | ASTMD638 | 43.0 MPa |
| 拉伸应力 | Yield | ISO527-2/50 | 43.0 MPa |
| 抗张强度 | Break | ASTMD638 | 26.0 MPa |
| 拉伸应力 | Break | ISO527-2/50 | 31.0 MPa |
| 伸长率 | Break | ASTMD638 | 17 % |
| 拉伸应变 | Break | ISO527-2/50 | 11 % |
| 弯曲模量 | ASTMD790 | 1700 MPa | |
| ISO178 | 1760 MPa | ||
| 弯曲强度 | ASTMD790 | 49.0 MPa | |
| 弯曲应力 | ISO178 | 49.0 MPa |
| 可燃性 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL阻燃等级 | 3.0mm | UL94 | HB |
| 硬度 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 洛氏硬度 | R-Scale | ASTMD785 | 95 |
| R-Scale | ISO2039-2 | 95 |
| 冲击性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 悬壁梁缺口冲击强度 | 23°C | ISO180/1A | 40 kJ/m² |
| 热变形温度 | 1.8MPa,Unannealed,4.00mm | ISO75-2/A | 73.0 °C |
| 1.8MPa,Annealed,4.00mm | ISO75-2/A | 89.0 °C | |
| 维卡软化温度 | -- | ISO306/B50 | 90.0 °C |
| -- | ISO306/B120 | 94.0 °C | |
| 热变形温度 | 0.45MPa,未退火,6.40mm | ASTMD648 | 95.0 °C |
| 0.45MPa,Unannealed,4.00mm | ISO75-2/B | 85.0 °C | |
| 0.45MPa,Annealed,4.00mm | ISO75-2/B | 97.0 °C | |
| 1.8MPa,未退火,6.40mm | ASTMD648 | 80.0 °C | |
| 悬壁梁缺口冲击强度 | 23°C,3.18mm | ASTMD256 | 390 J/m |
| 23°C,6.35mm | ASTMD256 | 200 J/m |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.