PBT 450-FR/GF30
0
- Properties:Fillerglass fiber reinforced material30%filler by weight
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.65 g/cm³ | |
| Shrinkage rate | ISO 294-4 | 0.20 % | |
| ISO 294-4 | 1.00 % | ||
| Water absorption rate | ISO 62 | 0.40 % | |
| ISO 62 | 0.10 % | ||
| melt mass-flow rate | ISO 1133 | 10 cm³/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ISO 527-2 | 130 MPa | |
| elongation at break | ISO 527-2 | 2 % | |
| Tensile modulus | ISO 527-2 | 10000 MPa | |
| Charpy Notched Impact Strength | ISO 179/1eA | 7.50 kJ/m² | |
| Impact strength of simply supported beam without notch | ISO 179/1eU | 50 kJ/m² |
| Flame retardant performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL -94 | V-0 1.50mm | |
| UL -94 | V-0 3.00mm |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | 25 KV/mm | |
| Dissipation Factor | IEC 60112 | 200 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| vicat | ISO 306/A50 | 210 °C | |
| Melting Temperature | ISO 11357-3 | 224 °C | |
| Heat distortion temperature | ISO 75-2/Bf | 215 °C | |
| ISO 75-2/Af | 205 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.