Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ASTM D955 | 0.20-0.60 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 103 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| transmissivity | | ASTM D1003 | 91.0 % |
| transmissivity | | ASTM D1003 | 89.0 % |
| Haze ratio | | ASTM D1003 | 0.30 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| 23°C | | ISO 178 | 65.0 Mpa |
| Surrender, 23 ° C | | ASTM D790 | 69.0 Mpa |
| Tensile modulus | | ISO 527-2 | 1800 Mpa |
| Surrender, 23 ° C | | ASTMD638 | 47.0 Mpa |
| Fracture, 23 ° C | | ASTM D638 | 51.0 Mpa |
| Fracture, 23 ° C | | ISO 527-2 | 46.0 Mpa |
| Surrender, 23 ° C | | ASTM D638 | 5.0 % |
| Surrender, 23 ° C | | ISO 527-2 | 4.0 % |
| Fracture, 23 ° C | | ASTM D638 | 300 % |
| Fracture, 23 ° C | | ISO 527-2 | 200 % |
| 23°C | | ASTM D790 | 2000 Mpa |
| 23°C | | ISO 178 | 1850 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| -40°C | | ASTM D256 | 40 J/m |
| 23°C | | ASTM D256 | 80 J/m |
| -40°C | | ISO 180 | 4.8 kJ/m² |
| 23°C | | ISO 180 | 7.8 kJ/m² |
| Suspended wall beam without notch impact strength | | ASTM D4812 | 无断裂 |
| Suspended wall beam without notch impact strength | | ASTM D4812 | 无断裂 |
| Dart impact | | ASTM D3763 | 48.0 J |
| Dart impact | | ASTM D3763 | 42.0 J |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 74.0 °C |
| Heat distortion temperature | | ASTM D648 | 65.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.