Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | Saturation | ASTM D570 | <0.040 % |
| density | | ASTM D792 | 1.40 g/cm³ |
| Water absorption rate | | ASTM D570 | <0.040 % |
| density | | ASTM D792 | 1.40 g/cm³ |
| Water absorption rate | | ASTM D570 | <0.040 % |
| Water absorption rate | Saturation | ASTM D570 | <0.040 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ASTM D2240 | 89 |
| Shore hardness | | ASTM D2240 | 89 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| UL flame retardant rating | | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 3210 MPa |
| tensile strength | Ultimate | ASTM D638 | 57.6 MPa |
| bending strength | Yield | ASTM D790 | 57.6 MPa |
| Compression Modulus | | ASTM D695 | 2410 MPa |
| elongation | Break | ASTM D638 | 5.0 % |
| Flexural modulus | | ASTM D790 | 2740 MPa |
| bending strength | Yield | ASTM D790 | 57.6 MPa |
| Compression Modulus | | ASTM D695 | 2410 MPa |
| compressive strength | | ASTM D695 | 82.7 MPa |
| elongation | Break | ASTM D638 | 5.0 % |
| Flexural modulus | | ASTM D790 | 2740 MPa |
| compressive strength | | ASTM D695 | 82.7 MPa |
| Tensile modulus | | ASTM D638 | 3210 MPa |
| tensile strength | Ultimate | ASTM D638 | 57.6 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256A | 21 J/m |
| Impact strength of cantilever beam gap | | ASTM D256A | 21 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ASTM D257 | >1.0E+12 ohms |
| Surface Resistivity | | ASTM D257 | >1.0E+12 ohms |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Maximum operating temperature LongTerm, Air | | | 60 °C |
| Maximum operating temperature LongTerm, Air | | | 60 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.