PA66 TAROMID A 280 Z3 Taro Plast S.p.A.

Product Description

Certificates(0)

Datasheet

Product Description

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	23°C	ISO 179/1eA	55	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C3	ASTM D256	55	kJ/m²
Impact strength of cantilever beam gap	-25°C,3.20mm	ASTMD256	640	J/m
	Impact strength of cantilever beam gap	23°C,3.20mm	ASTMD256	700	J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C4	ISO 180/1A	60	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.0mm	UL 94	HB
	UL flame retardant rating	1.6mm	UL 94	HB
	UL flame retardant rating	UL flame retardant rating	3.2mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	--	ISO 178	75.0	MPa
bending strength	bending strength	Break	ASTM D790	75.0	MPa
Tensile modulus		ASTMD638	2400	MPa
tensile strength	Yield	ASTMD638	55.0	MPa
elongation	Break	ASTMD638	50	%
Bending modulus		ASTMD790	2000	MPa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Ball Pressure Test	125°C	VDE0470	通过
Hot deformation temperature	1.8MPa,Unannealed	ASTMD648	66.0	°C
Vicat softening temperature		ISO 306/B50	210	°C
Melting temperature		ASTMD211	256	°C
Linear coefficient of thermal expansion	MD：-30to30°C	ASTM D696	7E-05	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTMD792	1.08	g/cm³
Shrinkage rate	MD	ASTM D955	1.5to1.7	%
Water absorption rate	23°C,24hr	ASTMD570	1.2	%
	Water absorption rate	Saturation	ASTM D570	6.0	%
	Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	6.0	%
GranuleHumidity		Internal Method	<0.15	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		ASTM D257	1E+15	ohms·cm
Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.