PP HM562S BASELL THAILAND

Form：Granules | Grade：Extrusion grade

Properties:

Narrow molecular weight dIt is a metallocene catalSuitable for extrusion ap

Typical Applications:

Non-woven fabricBCF filamentspunbond

Supplier(0)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Non-woven fabric \| BCF filament \| spunbond
Properties:	Narrow molecular weight d \| It is a metallocene catal \| Suitable for extrusion ap

Certificates

No Data...

Technical Data Sheet

Basic Performance	Test Condition	Test Method	Test Result	Test Unit
Melt Volume Flow Rate (MVR)	230°C/2.16 kg	ISO 1133	40	CM
melt mass-flow rate	230°C/2.16 kg	ISO 1133	30	g/10min
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23℃	ISO 179	2
Bending modulus	23℃	ISO 178	1400	Mpa
Tensile strain	Break 23℃	ISO 527-1	50	%
Tensile strain	Tensile strain	Yield 23℃	ISO 527-1	10	%
tensile strength	Yield 23℃	ISO 527-1	31	Mpa
Tensile modulus	23℃	ISO 527-1	1450	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Melting temperature	DSC	ISO 3146	145	°C
Vicat softening temperature	B50 (50°C/h 10N)	ISO 306	82	°C
Vicat softening temperature	Vicat softening temperature	A50 (50°C/h 10N)	ISO 306	136	°C
Hot deformation temperature	0.45Mpa, Unannealed	ISO 75B-1	93	°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.