TSU-Ether InnoTuf® HP-2140A Innovative Polymers, Inc.
0
CompareTechnical Data Sheet
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Viscosity | 0.63 Pa·s | ||
| 1.7E+02 hr | |||
| 20to30 min | |||
| 0.13 Pa·s | |||
| 0.48 Pa·s |
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | 1.03 g/cm³ | ||
| 1.04 g/cm³ | |||
| Base Resin | 1.06 g/cm³ | ||
| Shrinkage rate | ASTM D2566 | 0.20to0.50 % |
| thermosetting | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Thermosetting components | Resin | 按重量计算的混合比:100按容量计算的混合比:100 | |
| Hardener | 按重量计算的混合比:47按容量计算的混合比:50 | ||
| Demold Time | 300to420 min |
| Cured Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ASTM D638 | 4.14 MPa | |
| elongation | Break | ASTM D638 | 480 % |
| tear strength | ASTM D624 | 16.6 kN/m | |
| Shore hardness | ASTM D2240 | 35to45 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.