Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.25 g/cm³ |
| Melt volume flow rate | | ISO1133 | 26.0 cm³/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO868 | 62 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Flammability level | | IEC60695-11-10,-20 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile stress | | ISO527-2 | 17.1 MPa |
| Tensile stress | | ISO527-2 | 22.1 MPa |
| Tensile stress | | ISO527-2 | 22.9 MPa |
| Tensile stress | | ISO527-2 | 22.1 MPa |
| Nominal tensile fracture strain | | ISO527-2 | 370 % |
| Tensile modulus | | ISO527-2 | 430 MPa |
| Tensile stress | Break | ISO527-2 | 35.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 7.0 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1eA | 23 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/1A | 5.0 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/1A | 21 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| melting temperature | | ISO11357-3 | 221 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare