Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ASTM D570 | <0.010 % |
| melt mass-flow rate | | JISK6719 | 12 g/10min |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| gloss | | | - |
| Fuzzy coefficient (Haze) | | ISO 14782 | - % |
| transmittance | | ASTM D1003/ISO 13468 | 92 % |
| refractive index | | ASTM D542/ISO 489 | 1.509 |
| refractive index | | ASTM D542 | 1.509 |
| transmissivity | | ASTM D1003 | 92.0 % |
| other | Test Condition | Test Method | Test Result |
|---|
| characteristic | | | 耐化学系.防潮.抗紫外线良好.良好的成型性能。 |
| Color | | | 透明 |
| purpose | | | 光学应用、相机、印刷机。 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ASTM D256/ISO 179 | 10.8 kg·cm/cm(J/M)ft·lb/in |
| Charpy Notched Impact Strength | | ASTM D256/ISO 179 | - kg·cm/cm(J/M)ft·lb/in |
| Impact strength of cantilever beam gap | | ASTM D256/ISO 179 | - kg·cm/cm(J/M)ft·lb/in |
| elongation at break | | ASTM D638/ISO 527 | - kg/cm²(MPa)[Lb/in²] |
| elongation | | ASTM D638/ISO 527 | 2 % |
| Flexural modulus | | ASTM D790/ISO 178 | 2750 kg/cm²(MPa)[Lb/in²] |
| bending strength | | ASTM D790/ISO 178 | 65 kg/cm²(MPa)[Lb/in²] |
| tensile strength | | ASTM D638/ISO 527 | 32 kg/cm²(MPa)[Lb/in²] |
| Tensile modulus | | ASTM D638/ISO 527 | 1770 kg/cm²(MPa)[Lb/in²] |
| tensile strength | | ISO 527-2 | 45.0 Mpa |
| Tensile strain | | ISO 527-2 | 3.0 % |
| Flexural modulus | | ISO 178 | 3100 Mpa |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792/ISO 1183 | 0.948 |
| Shrinkage rate | | ASTM D955 | - % |
| melt mass-flow rate | | ASTM D1238/ISO 1133 | 32 g/10min |
| melt mass-flow rate | | ASTM D1238/ISO 1133 | - g/10min |
| Water absorption rate | | ASTM D570/ISO 62 | 0.01 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Glass Transition Temperature | | ASTM D785 | 123 ℃（℉） |
| Heat distortion temperature | | ASTM D648/ISO 75 | 110 ℃（℉） |
| Heat distortion temperature | | ASTM D648/ISO 75 | - ℃（℉） |
| Combustibility (rate) | | UL 94 | HB |
| Glass Transition Temperature | | JISK7121 | 123 °C |
| Linear coefficient of thermal expansion | | ASTME831 | 7E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.