HIPS STAREX® NH-1926 K2134
28
- Properties:TougheningThermal stability
- Usages:Automotive componentsElectronic and Electrical Applications
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | IS0 62 | 0.8 % | |
| density | ISO 1183 | 1.10 g/cm³ |
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | ISO 167 | 10¹³ Ohm | |
| dielectric strength | IEC1183 | 20 KV/mm | |
| Linear forming shrinkage rate | ISO2577 | 0.009-0.013 mm/mm |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile strength at break | IS0527 | 60 Mpa | |
| elongation at break | IS0527 | 40 % | |
| Yield bending strength | IS0178 | 80 Mpa | |
| Flexural modulus | IS0 178 | 1900 Mpa | |
| Charpy Notched Impact Strength | ISO 179/1eA | 24 kJ/m² | |
| Simple support without notch impact strength | ISO 179/1eU | NB kJ/m² | |
| Rockwell hardness | 110 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | IS0 75 | 140 ℃ | |
| IS0 75 | 55 ℃ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.