Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | DIN 53464 | 0.0 % |
| Water absorption rate | | ISO 62 | <0.50 % |
| Shrinkage rate | | ISO 2577 | 0.15 % |
| density | | ISO 1183 | 1.70 g/cm³ |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Hot filament ignition temperature | | IEC 60695-2-13 | 750 °C |
| Limiting Oxygen Index | | ISO 4589-2 | 27 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| GlowBar | | IEC 60707-3 | LevelBH2<=95 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | Compression Molded | ISO 527-2 | 11000 MPa |
| tensile strength | | ISO 527-2 | 60.0 MPa |
| Flexural modulus | Compression Molded | ISO 178 | 9000 MPa |
| bending strength | Compression Molded | ISO 178 | 142 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | Compression Molded | ISO 179 | 64 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | 1E+12 ohms |
| Volume resistivity | | IEC 60093 | 1E+15 ohms·cm |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/A | >200 °C |
| Continuous use temperature | | 内部方法 | 165 °C |
| Glass Transition Temperature | | DSC | 170 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 1.2E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.