Technical Data Sheet
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| Thermosetting components | | | 按重量计算的混合比:1.0 |
| Thermosetting components | | | 按重量计算的混合比:1.0 |
| Thermosetting components | | | 4.0 hr |
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|
| Color | | | Translucent |
| Color | | | Translucent |
| Viscosity | | DIN 53019 | 1000 Pa·s |
| Viscosity | | DIN 53019 | 1000 Pa·s |
| Viscosity | | DIN 53019 | 4300 min |
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | DIN 53479 | 1.14 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | Shore A | DIN 53505 | 70 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| sulfurization | | | 10.0 min |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| tear strength | | ASTM D624 | 20.0 kN/m |
| compression set | | ISO 815 | 25 % |
| tensile strength | | DIN 53504 | 9.00 MPa |
| elongation | Break | DIN 53504 | 400 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.