Technical Data Sheet
physical property | Test Condition | Test Method | Test Result |
---|
density | | ASTM D792 | 1.20 g/cm³ |
melt mass-flow rate | | ASTM D1238 | 9.0 g/10min |
Shrinkage rate | | ASTM D955 | 0.20to0.50 % |
Water absorption rate | | ASTM D570 | 0.060 % |
hardness | Test Condition | Test Method | Test Result |
---|
Rockwell hardness | | ASTM D785 | 106 |
flammability | Test Condition | Test Method | Test Result |
---|
UL flame retardant rating | | UL 94 | HB |
Limiting Oxygen Index | | ASTM D2863 | 26 % |
Impact resistance | Test Condition | Test Method | Test Result |
---|
Impact strength of cantilever beam gap | | ASTM D256 | 120 J/m |
Suspended wall beam without notch impact strength | | ASTM D256 | 650 J/m |
Impact strength of cantilever beam gap | | ASTM D256 | 96 J/m |
Dart impact | | ASTM D3763 | 22.6 J |
Mechanical properties | Test Condition | Test Method | Test Result |
---|
Tensile modulus | | ASTM D638 | 6200 MPa |
tensile strength | Break | ASTM D638 | 90.3 MPa |
elongation | Break | ASTM D638 | 2.6 % |
Flexural modulus | | ASTM D790 | 5800 MPa |
bending strength | | ASTM D790 | 160 MPa |
Electrical performance | Test Condition | Test Method | Test Result |
---|
dielectric strength | | ASTM D149 | 17 kV/mm |
dielectric constant | | ASTM D150 | 2.86 |
dielectric constant | | ASTM D150 | 2.86 |
Dissipation Factor | | ASTM D150 | 8E-04 |
arc resistance | | ASTM D495 | PLC7 |
High arc combustion index (HAI) | | UL 746 | PLC 4 |
High Voltage Arc Traceability Rate (HVTR) | | UL 746 | PLC 4 |
Hot wire ignition (HWI) | | UL 746 | PLC 4 |
Dissipation Factor | | ASTM D150 | 8E-04 |
Thermal performance | Test Condition | Test Method | Test Result |
---|
RTI Imp | | UL 746 | 90.0 °C |
RTI | | UL 746 | 90.0 °C |
Heat distortion temperature | | ASTM D648 | 143 °C |
Heat distortion temperature | | ASTM D648 | 135 °C |
Heat distortion temperature | | ASTM D648 | 138 °C |
Linear coefficient of thermal expansion | | ASTME831 | 2.9E-05 cm/cm/°C |
Linear coefficient of thermal expansion | | ASTME831 | 8.3E-05 cm/cm/°C |
RTI Elec | | UL 746 | 90.0 °C |
Heat distortion temperature | | ASTM D648 | 141 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.