Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTMD1238 | 5.6 g/10min |
| melt mass-flow rate | | ISO1133 | 18 g/10min |
| Shrinkage rate | | 内部方法 | 0.50to0.80 % |
| melt viscosity | | ASTMD3835 | 225 Pa·s |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTMD785 | 112 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTMD638 | 2270 Mpa |
| Tensile modulus | | ISO527-2/1 | 2370 Mpa |
| tensile strength | | ASTMD638 | 44.0 Mpa |
| Tensile stress | | ISO527-2/50 | 47.0 Mpa |
| tensile strength | | ASTMD638 | 33.0 Mpa |
| Tensile stress | | ISO527-2/50 | 35.0 Mpa |
| elongation | | ASTMD638 | 2.0 % |
| Tensile strain | | ISO527-2/50 | 2.6 % |
| elongation | | ASTMD638 | 24 % |
| Tensile strain | | ISO527-2/50 | 25 % |
| Flexural modulus | | ASTMD790 | 2300 Mpa |
| Flexural modulus | | ISO178 | 2200 Mpa |
| Bending strength 5,6 | | ISO178 | 70.0 Mpa |
| bending strength | | ASTMD790 | 70.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam gap 7 | | ISO179/1eA | 9.0 kJ/m² |
| Impact strength of simply supported beam gap 7 | | ISO179/1eA | 26 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/1A | 8.0 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/1A | 22 kJ/m² |
| Dart impact equipped with measuring instruments | | ASTMD3763 | 30.0 J |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| High Voltage Arc Traceability Rate (HVTR) | | UL746 | PLC 3 |
| Hot wire ignition (HWI) | | UL746 | PLC 3 |
| Arc resistance 11 | | ASTMD495 | PLC6 |
| Compared to the Leakage Tracking Index (CTI) | | UL746 | PLC 0 |
| High arc combustion index (HAI) | | UL746 | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ISO306/B50 | 98.0 °C |
| vicat | | ISO306/B120 | 100 °C |
| | ASTME831 | 8.8E-05 cm/cm/°C |
| | ASTME831 | 8.8E-05 cm/cm/°C |
| RTI Elec | | UL746 | 60.0 °C |
| RTI Imp | | UL746 | 60.0 °C |
| RTI Str | | UL746 | 60.0 °C |
| | ASTMD648 | 94.0 °C |
| | ASTMD648 | 80.0 °C |
| Hot deformation temperature 9 | | ISO75-2/Af | 81.0 °C |
| vicat | | ASTMD152510 | 99.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.