Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | g/cm³ | 1.23 -- |
| Shrinkage rate | | % | 1.0 -- |
| Shrinkage rate | | % | 0.60 -- |
| Water absorption rate | | % | 7.0 -- |
| Water absorption rate | | % | 2.3 -- |
| viscosity number | | cm³/g | 145 -- |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | | HB -- |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | kJ/m² | 7.0 7.0 |
| Charpy Notched Impact Strength | | kJ/m² | 8.0 11 |
| Impact strength of simply supported beam without notch | | kJ/m² | 38 38 |
| Impact strength of simply supported beam without notch | | kJ/m² | 40 60 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | MPa | 6100 4200 |
| tensile strength | Yield | MPa | 140 80.0 |
| tensile strength | Break | MPa | 130 85.0 |
| Tensile strain | Yield | % | 3.5 12 |
| Tensile strain | Break | % | 3.0 10 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Compared to the Leakage Tracking Index (CTI) | | V | PLC 1 |
| Surface Resistivity | | ohms | 1E+10 -- |
| Volume resistivity | | ohms·cm | 1E+15 -- |
| | | 3.50 -- |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Hot deformation temperature (HDT) | | °C | 250 -- |
| Hot deformation temperature (HDT) | | °C | 235 -- |
| Hot deformation temperature (HDT) | | °C | 70.0 -- |
| melting temperature | | °C | 260 -- |
| | cm/cm/°C | 3.4E-05 -- |
| | cm/cm/°C | 7E-05 -- |
| Hot deformation temperature (HDT) | | °C | <400 <400 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.