PP 7H2W-V0 LATI ITALY

Form：Granules | Grade：Flame retardant grade

Supplier(1)

Product Description

Certificates(0)

Datasheet

Alternative(4)

Product Description

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	-20°C	ISO 179/1eU	20	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	25	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
Burning wire flammability index	1.0mm	IEC 60695-2-12	960	°C
Burning wire flammability index	Burning wire flammability index	2.0mm	IEC 60695-2-12	960	°C
Hot filament ignition temperature	1.0mm	IEC 60695-2-13	825	°C
Hot filament ignition temperature	Hot filament ignition temperature	2.0mm	IEC 60695-2-13	825	°C
Extreme Oxygen Index		ASTM D2863	33	%
UL flame retardant rating	0.75mm	UL 94	V-2
	UL flame retardant rating	1.5mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	23°C	ISO 527-2/1	1800	Mpa
	Tensile modulus	60°C	ISO 527-2/1	800	Mpa
	Tensile modulus	Tensile modulus	90°C	ISO 527-2/1	500	Mpa
tensile strength	Yield,23°C	ISO 527-2/5	20.0	Mpa
	tensile strength	Yield,60°C	ISO 527-2/5	10.0	Mpa
		tensile strength	Yield,90°C	ISO 527-2/5	7.00	Mpa
		tensile strength	tensile strength	Break,23°C	ISO 527-2/5	15.0	Mpa
Tensile strain	Yield,23°C	ISO 527-2/5	5.0	%
	Tensile strain	Yield,60°C	ISO 527-2/5	>10	%
		Tensile strain	Yield,90°C	ISO 527-2/5	>10	%
			Tensile strain	Break,23°C	ISO 527-2/5	20	%
				Tensile strain	Break,60°C	ISO 527-2/5	>100	%
				Tensile strain	Tensile strain	Break,90°C	ISO 527-2/5	>100	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	110	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	65.0	°C
Continuous use temperature			100	°C
Vicat softening temperature		ISO 306/B50	100	°C
Linear coefficient of thermal expansion	MD：30to100°C	ISO 11359-2	8E-05	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	TD:2.00mm	ISO 294-4	1.2-1.5	%
Shrinkage rate	Shrinkage rate	MD:2.00mm	ISO 294-4	1.2-1.5	%
Water absorption rate	23°C,24hr	ISO 62	0.070	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 0
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
dimensional stability			70.0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.