PA66 Vydyne® 22HSP NT

Usages:
Bushings
bearings
casings
cams
industrial applications
connectors
Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
Water absorption rate		ISO 62	1.2 %
Water absorption rate	Water absorption rate		ISO 62	2.4 %
density		ISO 1183	1.14 g/cm³
Shrinkage rate		ISO 294-4	2.0 %
Shrinkage rate	Shrinkage rate		ISO 294-4	2.2 %

Mechanical properties	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap		ISO 180/1A	5.0 kJ/m²
tensile strength		ISO 527-2	85 MPa
tensile strength	tensile strength		ISO 527-2	55 MPa
elongation at break		ISO 527-2	5.0 %
elongation at break	elongation at break		ISO 527-2	25 %
Tensile modulus		ISO 527-2	3100 MPa
Tensile modulus	Tensile modulus		ISO 527-2	0.40
bending strength		ISO 178	95 MPa
Flexural modulus		ISO 178	2900 MPa
Charpy Notched Impact Strength		ISO 179/1eA	6.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength		ISO 179/1eA	5.0 kJ/m²
Impact strength of simply supported beam without notch		ISO 179/1eU	NB kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch		ISO 179/1eU	NB kJ/m²
Impact strength of cantilever beam gap		ISO 180/1A	6.0 kJ/m²

Flame retardant performance	Test Condition	Test Method	Test Result
UL flame retardant rating		UL -94	V-2 0.71mm
	UL flame retardant rating		UL -94	V-2 1.50mm
	UL flame retardant rating	UL flame retardant rating		UL -94	V-2 3.00mm
Limiting Oxygen Index		ISO 4589-2	23 %

Electrical performance	Test Condition	Test Method	Test Result
Dissipation Factor		IEC 61621	60-119 s
Dissipation Factor	Dissipation Factor		IEC 60112	400-599 V

Thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature (HDT)		ISO 75-2/Bf	200 °C
Hot deformation temperature (HDT)	Hot deformation temperature (HDT)		ISO 75-2/Af	70 °C
		ISO 11359-2	1E-05 cm/cm／°C
			ISO 11359-2	1E-05 cm/cm／°C
linear expansion coefficient		ISO 11359-2	260 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.