Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTMD1238 | 6.0to13 g/10min |
| density | | ASTMD792 | 1.19 g/cm³ |
| melt mass-flow rate | | ASTMD1238 | 2.0to5.0 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore A | ASTMD2240 | 85 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| UL flame retardant rating | | UL94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | Injection | ASTMD412 | 20.7 MPa |
| Flexural modulus | Injection | ASTMD790 | 24.8 MPa |
| | ASTMD1044 | 25.0 mg |
| Abrasion-DIN | | DIN53516 | 25 mm³ |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| Tensile stress | | ASTMD412 | 6.89 MPa |
| Tensile stress | | ASTMD412 | 15.2 MPa |
| tensile strength | | ASTMD412 | 41.4 MPa |
| elongation | Break | ASTMD412 | 590 % |
| tear strength | | ASTMD624 | 109 kN/m |
| compression set | | ASTMD395B | 25 % |
| compression set | | ASTMD395B | 35 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Glass Transition Temperature | | 内部方法 | -40.0 °C |
| vicat | | ASTMD1525 | 110 °C |
| SofteningPoint-DMA | | 内部方法 | 100 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.