PC+AS(SAN) LNP™ LUBRILOY™ Lexan_WR6300 compound

Usages:
Business equipment
Compare

Technical Data Sheet

physical property	Test Method	Test Result
Shrinkage rate	内部方法	0.50到0.70 %
density	ASTMD792	1.17 g/cm³
Melt volume flow rate	ISO1133	38.0 cm³/10min
Shrinkage rate	内部方法	0.50to0.70 %
density	ASTMD792	1.17 g/cm³
Melt volume flow rate	ISO1133	38.0 cm³/10min

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL94	HB
UL flame retardant rating	UL flame retardant rating		UL94	HB

Mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Yield	ASTMD638	60.7 MPa
tensile strength	tensile strength	Break	ASTMD638	61.4 MPa
elongation	Break	ASTMD638	160 %
Flexural modulus		ASTMD790	2490 MPa
bending strength		ASTMD790	96.5 MPa
tensile strength	Yield	ASTMD638	60.7 MPa
tensile strength	tensile strength	Break	ASTMD638	61.4 MPa
elongation	Break	ASTMD638	160 %
Flexural modulus		ASTMD790	2490 MPa
bending strength		ASTMD790	96.5 MPa

Impact resistance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap		ASTMD256	170 J/m
	Impact strength of cantilever beam gap		ASTMD256	680 J/m
		Impact strength of cantilever beam gap		ASTMD256	170 J/m
			Impact strength of cantilever beam gap		ASTMD256	680 J/m
			Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ASTMD4812	2500 J/m
Dart impact equipped with measuring instruments		ASTMD3763	60.2 J
Suspended wall beam without notch impact strength		ASTMD4812	2500 J/m
Dart impact equipped with measuring instruments		ASTMD3763	60.2 J

Thermal performance	Test Method	Test Result
vicat	ASTMD15254	137 °C
	ASTME831	1.1E-04 cm/cm/°C
		ASTME831	1.2E-04 cm/cm/°C
			ASTMD648	134 °C
				ASTMD648	117 °C
					ASTMD648	121 °C
RTI Str	UL746	80.0 °C
	ASTMD648	134 °C
		ASTMD648	117 °C
			ASTMD648	121 °C
RTI Elec	UL746	80.0 °C
RTI Imp	UL746	80.0 °C
vicat	ASTMD15255	137 °C
	ASTME831	1.1E-04 cm/cm/°C
		ASTME831	1.2E-04 cm/cm/°C
RTI Elec	UL746	80.0 °C
RTI Imp	UL746	80.0 °C
RTI	UL746	80.0 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.