Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| SpiralFlow | | 内部方法 | 22.0 cm |
| Shrinkage rate | | 内部方法 | 0.19 % |
| Shrinkage rate | | 内部方法 | 0.17 % |
| density | | ISO1183 | 1.43 g/cm³ |
| Melt volume flow rate | | ISO1133 | 8.00 cm³/10min |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | 5VB |
| UL flame retardant rating | | UL94 | V-1 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| ISO Shortcut | | | >PC+AS-(TD+PD)30-FR(40)< |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179 | 3.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile stress | Yield | ISO527-2 | 74.0 MPa |
| Nominal tensile fracture strain | | ISO527-2 | 1.5 % |
| Flexural modulus | | ISO178 | 9000 MPa |
| Bending stress | | ISO178 | 113 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/A | 100 °C |
| | ISO11359-2 | 2.3E-05 cm/cm/°C |
| | ISO11359-2 | 4.5E-05 cm/cm/°C |
| RTI Elec | | UL746 | 50.0 °C |
| RTI Imp | | UL746 | 50.0 °C |
| RTI Str | | UL746 | 50.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare