Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.21 g/cm³ |
| melt mass-flow rate | | | 5.0to17 g/10min |
| Shrinkage rate | | ASTM D955 | 0.50to0.60 % |
| Water absorption rate | | ASTM D570 | 0.15 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ISO 868 | 83 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| transmissivity | | ASTM D1003 | 92.0 % |
| Yellowness Index | | ASTM D1925 | 15 YI |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO 180/1A | 5.7 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/1A | 8.2 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2/1A/1 | 2130 MPa |
| tensile strength | Yield | ISO 527-2/1A/5 | 63.0 MPa |
| tensile strength | Break | ISO 527-2/1A/5 | 64.0 MPa |
| Tensile strain | Yield | ISO 527-2/1A/5 | 7.0 % |
| Tensile strain | Break | ISO 527-2/1A/5 | 170 % |
| Flexural modulus | | ISO 178 | 1980 MPa |
| bending strength | | ISO 178 | 85.0 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 79.0 °C |
| Heat distortion temperature | | ISO 75-2/A | 69.0 °C |
| Glass Transition Temperature | | DSC | 90.0 °C |
| vicat | | ISO 306/A50 | 96.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.