ABS TR-558AI
40
- Properties:High impact resistancetransparenthigh strengthHigh strength
- Usages:Electronic fieldElectrical field
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ASTM D-955 | 0.4～0.7 % | |
| density | ASTM D-792 | 1.11 | |
| melt mass-flow rate | ASTM D-1238（G） | 2.2 g/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Stretching rate (breaking point) | ASTM D-638 | 40 % | |
| Tension measurement | ASTM D-638 | 22200（2180） kg/cm | |
| ASTM D-785 | 112 | ||
| bending strength | ASTM D-790 | 800（78） kg/cm | |
| IZOD impact strength | ASTM D-256 | 10(100) kg.cm/cm(J/m) | |
| Stretching rate (resistance point) | ASTM D-638 | ≥6 % | |
| Tensile strength | ASTM D-638 | 520（51） kg/cm | |
| Bending modulus | ASTM D-790 | 25000(2450) kg/cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| combustibility | IEC707 | - mm/min | |
| ASTM D-648 | 95(90) °C | ||
| Hot deformation temperature | ASTM D-648 | 89(89) °C | |
| Microcard softening point | ASTM D-1525 | 100(93) °C | |
| combustibility | UL-94 | HB CLASS |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.