TPE 5526 DUPONT USA

103

Form：Granules | Grade：Injection grade

Properties:

Weather resistanceUV resistanceHigh mobilityThermal stability

Typical Applications:

Automotive sectorElectrical appliancesFitness equipmentElectronic fieldElectrical field

Supplier(1)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	Automotive sector \| Electrical appliances \| Fitness equipment \| Electronic field \| Electrical field
Properties:	Weather resistance \| UV resistance \| High mobility \| Thermal stability

Certificates

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	23°C	ISO 8256/1	270	kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	NoBreak
Charpy Notched Impact Strength	-40°C	ISO 179/1eA	30	kJ/m²
	Charpy Notched Impact Strength	-30°C,Partial Break	ISO 179/1eA	150	kJ/m²
	Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	NoBreak
flammability	Test Condition	Test Method	Test Result	Test Unit
FMVSS flammability		FMVSS302	SE/B
Fogging-G-value	condensate	ISO 6452	1E-04	g
Extreme Oxygen Index		ISO 4589-2	21	%
UL flame retardant rating	3.0mm	IEC 60695-11-10,-20	HB
	UL flame retardant rating	1.5mm	IEC 60695-11-10,-20	HB
		UL flame retardant rating	3.0mm	UL 94	HB
		UL flame retardant rating	UL flame retardant rating	1.5mm	UL 94	HB
Burning rate	1.00mm	ISO 3795	28	mm/min
elastomer	Test Condition	Test Method	Test Result	Test Unit
tear strength	横向Flow	ISO 34-1	130	kN/m
tear strength	tear strength	Flow	ISO 34-1	130	kN/m
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Nominal tensile fracture strain		ISO 527-2	780	%
Tensile strain	Break	ISO 527-2	>300	%
Tensile strain	Tensile strain	Yield	ISO 527-2	35	%
tensile strength	50%Strain	ISO 527-2	14.0	Mpa
	tensile strength	10%Strain	ISO 527-2	11.0	Mpa
		tensile strength	5.0%Strain	ISO 527-2	6.90	Mpa
			tensile strength	Break	ISO 527-2	40.0	Mpa
			tensile strength	tensile strength	Yield	ISO 527-2	15.0	Mpa
Tensile modulus		ISO 527-2	190	Mpa
Tensile creep modulus	1hr	ISO 899-1	170	Mpa
Tensile creep modulus	Tensile creep modulus	1000hr	ISO 899-1	130	Mpa
Bending modulus		ISO 178	200	Mpa
Wear resistance		ISO 4649	120	mm³
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature	--	ISO 306/A50	180	°C
Glass transition temperature		ISO 11357-2	-20.0	°C
Brittle temperature		ISO 974	-98.0	°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	45.0	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	65.0	°C
Vicat softening temperature	--	ISO 306/B50	75.0	°C
Melting temperature		ISO 11357-3	203	°C
Linear coefficient of thermal expansion	MD：--	ISO 11359-2	2E-04	cm/cm/°C
	Linear coefficient of thermal expansion	MD：-40to23°C	ISO 11359-2	1.8E-04	cm/cm/°C
		Linear coefficient of thermal expansion	TD：--	ISO 11359-2	2E-04	cm/cm/°C
			Linear coefficient of thermal expansion	TD：-40to23°C	ISO 11359-2	1.7E-04	cm/cm/°C
			Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：EffectiveThermalDiffusivity	ISO 11359-2	9E-08	m²/s
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	MD	ISO 294-4	1.4	%
Water absorption rate	23°C,24hr	ISO 62	0.60	%
Shrinkage rate	TD	ISO 294-4	1.4	%
Melt Volume Flow Rate (MVR)	220°C/2.16kg	ISO 1133	17.5	cm3/10min
melt mass-flow rate		ISO 1133	18	g/10min
density		ISO 1183	1.19	g/cm³
Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO 62	0.20	%
Water absorption rate	Water absorption rate	Saturation,23°C,2.00mm	ISO 62	0.60	%
SpecificHeatCapacity of Melt			2110	J/kg/°C
ThermalConductivityofMelt			0.19	W/m/K
MediumDensity			1.04	g/cm³
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		IEC 60093	>1.0E+15	ohms
Volume resistivity		IEC 60093	4E+13	ohms·cm
Dielectric strength		IEC 60243-1	20	KV/mm
Dissipation factor	1MHz	IEC 60250	0.038
Dissipation factor	Dissipation factor	100Hz	IEC 60250	9E-03
Relative permittivity	1MHz	IEC 60250	4.60
Relative permittivity	Relative permittivity	100Hz	IEC 60250	4.90
hardness	Test Condition	Test Method	Test Result	Test Unit
Shore hardness	ShoreD,15Sec	ISO 868	51
Shore hardness	Shore hardness	ShoreD	ISO 868	55
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
Odor		VDA270	5.00

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.