Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 0.905 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 7.5 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 98 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| gloss | | ASTM D2457 | 99 |
| Haze ratio | | ASTM D1003 | 1.8 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 33.0 MPa |
| elongation | | ASTM D638 | 13 % |
| Flexural modulus | Injection | ASTM D790 | 1400 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 30 J/m |
| film | Test Condition | Test Method | Test Result |
|---|
| Secant modulus | | ASTM D882 | 570 MPa |
| Secant modulus | | ASTM D882 | 580 MPa |
| tensile strength | Yield | ASTM D882 | 22.0 MPa |
| tensile strength | | ASTM D882 | 21.0 MPa |
| Tensile strain | | ASTM D882 | 12 % |
| Tensile strain | | ASTM D882 | 11 % |
| Initial sealing temperature | | | 115 °C |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 92.0 °C |
| Heat distortion temperature | | ASTM D648 | 52.0 °C |
| vicat | | ASTM D15252 | 148 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.