Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD1505 | 0.910 g/cm³ |
| melt mass-flow rate | | ASTMD1238 | 35 g/10min |
| Shrinkage rate | | 内部方法 | 1.4 % |
| Shrinkage rate | | 内部方法 | 1.3 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTMD785 | 80 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| gloss | | ASTMD2457 | 80 |
| Haze ratio | | ASTMD1003 | 12 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Melt Temperature | | ASTMD2117 | 150 °C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTMD256 | 54 J/m |
| Impact strength of cantilever beam gap | | ASTMD256 | 34 J/m |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Yield | ASTMD638 | 29.4 MPa |
| tensile strength | Break | ASTMD638 | 17.7 MPa |
| elongation | Break | ASTMD638 | 600 % |
| Flexural modulus | | ASTMD790 | 1230 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ASTMD648 | 90.0 °C |
| | ASTMD648 | 50.0 °C |
| brittle temperature | | ASTMD746 | -20.0 °C |
| vicat | | ASTMD1525 | 130 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare