Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.04 g/cm³ |
| Water absorption rate | | ASTM D570 | 0.10 % |
| Shrinkage rate | | ASTM D955 | 0.40 % |
| Shrinkage rate | | ASTM D955 | 0.40 % |
| melt mass-flow rate | | ASTM D1238 | 10 g/10min |
| melt mass-flow rate | | ASTM D1238 | 12 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ASTM D2240 | 92 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Burning wire flammability index | | IEC 60695-2-12 | 850 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 775 °C |
| Limiting Oxygen Index | | ISO 4589-2 | 24 % |
| UL flame retardant rating | | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| fracture | | ASTM D638 | 9.00 MPa |
| fracture | | ISO 527-2/50 | 9.00 MPa |
| fracture | | ASTM D638 | 120 % |
| fracture | | ISO 527-2/50 | 120 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| Dissipation Factor | | IEC 60250 | 6E-03 |
| relative permittivity | | IEC 60250 | 2.80 |
| dielectric strength | | IEC 60243-1 | 23 kV/mm |
| Volume resistivity | | ASTM D257 | 4E+15 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| brittle temperature | | ASTM D746 | <-40.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare