PARA IXEF® 1521/9008
51
- Properties:Creep resistancehigh strengthFiller: Glass fiber reinf50% filler by weight
- Usages:sporting goodsVehicle electronicsElectrical appliancesLawn and garden equipmentApplication in the automotive fieldBushingAircraft ApplicationsfurnitureIndustrial applicationsEngine partsMachine/mechanical componentsHome appliance componentsBusiness equipmentMetal substitutionCamera applicationsPower/Other Tools
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | 内部方法 | 0.10-0.30 % | |
| Water absorption rate | ISO 62 | 0.15 % | |
| Water absorption - Ejil, 65% RH | 内部方法 | 1.3 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 | |
| UL 94 | V-0 | ||
| UL 94 | 5VA | ||
| Burning wire flammability index | IEC 60695-2-12 | 960 °C | |
| IEC 60695-2-12 | 960 °C | ||
| IEC 60695-2-12 | 960 °C | ||
| Hot filament ignition temperature | IEC 60695-2-13 | 900 °C | |
| IEC 60695-2-13 | 930 °C | ||
| IEC 60695-2-13 | 900 °C | ||
| Limiting Oxygen Index | ISO 4589-2 | 32 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 20000 Mpa | |
| tensile strength | ISO 527-2 | 230 Mpa | |
| Tensile strain | ISO 527-2 | 1.9 % | |
| Flexural modulus | ISO 178 | 20000 Mpa | |
| bending strength | ISO 178 | 340 Mpa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Volume resistivity | IEC 60093 | >1.0E+13 ohms·cm | |
| dielectric strength | IEC 60243-1 | 29 KV/mm | |
| dielectric constant | IEC 60250 | 4.10 | |
| Dissipation Factor | IEC 60250 | 0.012 | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 1 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/A | 230 °C | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 1.7E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.