ABS/PA NM-11 INEOS STYRO KOREA

107

Form：Granules

Properties:

ProcessabilityHigh impact resistanceHigh mobility

Typical Applications:

Helmetsporting goodsShellAutomotive sectorApplication in the automotive field

Supplier(1)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	Helmet \| sporting goods \| Shell \| Automotive sector \| Application in the automotive field
Properties:	Processability \| High impact resistance \| High mobility

Certificates

FDA

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179	无断裂
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength	Yield,23°C	ISO 527-2	43.0	Mpa
Tensile modulus		ISO 527-2	2000	Mpa
bending strength		ISO 178	62.0	Mpa
Bending modulus		ISO 178	1800	Mpa
Tensile strain	Yield,23°C	ISO 527-2	3.5	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	MD	ISO 11359-2	1E-04	cm/cm/°C
Vicat softening temperature	--	ISO 306/B50	102	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/A50	160	°C
Hot deformation temperature	1.8MPa,Annealed	ISO 75-2/A	65.0	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Annealed	ISO 75-2/B	85.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	1.2	%
Shrinkage rate		ISO 294-4	0.80	%
Melt Volume Flow Rate (MVR)	240°C/10.0kg	ISO 1133	30.0	cm3/10min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dissipation factor	1MHz	IEC 60250	0.015
Relative permittivity	1MHz	IEC 60250	2.90
Volume resistivity		IEC 60093	>1.0E+15	ohms·cm
Surface resistivity		IEC 60093	1E+14	ohms
hardness	Test Condition	Test Method	Test Result	Test Unit
Ball Pressure Test		ISO 2039-1	86.0	Mpa
film	Test Condition	Test Method	Test Result	Test Unit
elongation	Break	ISO 527-3	>50	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.