| optical performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| turbidity | ASTM D1003 | 4.0 | % | |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| tear strength | ASTM D624 | 8.53 | Mpa | |
| Bending modulus | % Secant | ASTM D790 | 82.4 | Mpa |
| elongation | Break | ASTM D638 | 800 | % |
| tensile strength | Break | ASTM D638 | 24.5 | Mpa |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Melting temperature | Internal Method | 98.0 | °C | |
| Glass transition temperature | Internal Method | -31.0 | °C | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Mooney viscosity | ML 1+4, 121°C | ASTM D1646 | 20 | MU |
| melt mass-flow rate | 190°C/2.16 kg | ASTM D1238 | 1.0 | g/10 min |
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Shore hardness | Shore D, 1 Sec | ASTM D2240 | 40 | |
| Shore A, 1 Sec | ASTM D2240 | 92 | ||
| film | Test Condition | Test Method | Test Result | Test Unit |
| Elmendorf tear strength | TD : 50.0 μm | ASTM D1922 | 17 | g/µm |
| MD : 50.0 μm | ASTM D1922 | 10 | g/µm | |
| Initial sealing temperature | Blown Film | Internal Method | 80.0 | °C |
| Dart impact | 50 μm, Blown Film | ASTM D1709 | > 1000 | g |
| elongation | TD : Break, 50 μm, Blown Film | ASTM D882 | 620 | % |
| MD : Break, 50 μm, Blown Film | ASTM D882 | 600 | % | |
| tensile strength | TD : Break, 50 μm, Blown Film | ASTM D882 | 42.0 | Mpa |
| MD : Break, 50 μm, Blown Film | ASTM D882 | 47.0 | Mpa | |
| Secant modulus | 1% Secant, TD : 50 μm, Blown Film | ASTM D882 | 76.0 | Mpa |
| 1% Secant, MD : 50 μm, Blown Film | ASTM D882 | 68.0 | Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.