COC TOPAS® 8007S-04 DAICEL USA
397
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | (23°C,24hr) | ISO62 | 0.01 | % |
| Melt mass flow rate | 260℃/2.16Kg | ISO1133 | 32 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| tensile strength | 23°C | ISO527-2 | 63 | Mpa |
| elongation at break | 23°C | ISO527-2 | 4.5 | % |
| Tensile modulus | 23°C | ISO527-2 | 2600 | Mpa |
| Impact strength of simply supported beam gap | 23°C | ISO179/1eA | 2.6 | kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 20 | kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa未退火 | ISO75-2/Bf | 75 | °C |
| vicat softening point | ISO306/B50 | 80 | °C | |
| 玻璃转化温度 | ISO11357-2 | 78 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistance | IEC60093 | 1E+14 | Ω.cm | |
| Dielectric constant | 23°C | IEC60250 | 2.35 | 1kHz |
| Dissipation factor | 相对漏电起痕指数 | IEC60112 | 600 | V |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Refractive index | ISO489 | 1.53 | °C | |
| Transmittance 2000 μ m | ISO13468-2 | 91 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.