Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | g/cm³ | 1.37 -- |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | | 84 78 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Break | MPa | 175 115 |
| Tensile strain | Break | % | 4.0 6.0 |
| Flexural modulus | | MPa | 8100 4700 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | kJ/m² | 10 18 |
| Impact strength of simply supported beam without notch | | kJ/m² | 60 75 |
| Impact strength of cantilever beam gap | | kJ/m² | 12 21 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ohms·cm | 1E+15 1E+12 |
| dielectric strength | | kV/mm | 35 30 |
| Compared to the Leakage Tracking Index (CTI) | | V | PLC 1 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | °C | 230 -- |
| melting temperature | | °C | 243 -- |
| Linear coefficient of thermal expansion | | cm/cm/°C | 3.5E-05 -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.