PPA HTN51G45HSL DUPONT USA

Form：Granules | Grade：Injection grade

Properties:

High impact resistanceLow temperature resistancHigh temperature resistanFiller: Glass fiber reinf45% filler by weight

Typical Applications:

Automotive interior parts

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive interior parts
Properties:	High impact resistance \| Low temperature resistanc \| High temperature resistan \| Filler: Glass fiber reinf \| 45% filler by weight

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23℃	kJ/m²	4.178to19.964
flammability	Test Condition	Test Method	Test Result	Test Unit
Burning wire flammability index		°C	743to960
Extreme Oxygen Index		%	23to25
Hot filament ignition temperature		°C	721to926
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	摩擦系数		0.15to0.52
Yield, 23 ℃			68.97to250.34	MPa
Fracture, 23 ℃			131.72to400.0	MPa
	Fracture, 23 ℃		%	1.0to2.5
	Fracture, 23 ℃	Fracture, 23 ℃		%	1.5to3.1
Yield, 23 ℃		%	1.4to2.5
compressive strength	23℃		142.76to196.55	MPa
Poisson's ratio	23℃		0.41
Yield, 23 ℃			102.76to362.76	MPa
shear strength	23℃		88.28to107.59	MPa
Fracture, 23 ℃			162.76to199.31	MPa
Yield, 23 ℃		%	1.5to2.6
Yield, 23 ℃	Yield, 23 ℃			12.62to270.34	MPa
Fracture, 23 ℃			108.28to262.76	MPa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
flow		mm/mm/°C	185.4E-5-25.4E-5
1.8MPa, unannealed		°C	249to304
flow		mm/mm/°C	38.1E-5-50.8E-5
RTI Elec		°C	140to150
RTI Imp		°C	118to150
0.45MPa, unannealed		°C	273to312
transverse		mm/mm/°C	63.5E-5-177.8E-5
1.8MPa, annealed		°C	283to300
transverse		mm/mm/°C	68.6E-5-127.0E-5
flow		mm/mm/°C	195.6E-5-25.4E-5
Vicat softening temperature		°C	258to313
8.0Mpa, unannealed		°C	165to230
1.8MPa, unannealed		°C	247to292
0.45MPa, annealed		°C	296to320
0.45MPa, unannealed		°C	275to308
RTI		°C	119to150
Continuous use temperature		°C	140to186
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Flow: 23 ℃	Flow,23℃	mm/mm	48.3E-3-129.5E-3
23℃,24hr		%	0.12to0.30
Lateral flow: 23 ℃	Across Flow, 23℃	mm/mm	119.4E-3-0.254
Balance, 23 ℃, 50% RH		%	0.21to1.2
23℃,24hr		%	0.30to0.51
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Compared to the anti leakage trace index		V
Compared to the anti leakage trace index	Compared to the anti leakage trace index	CTI	V
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	23℃		125

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.