Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | | 0.60 - 0.80 % |
| Water absorption rate | | ASTM D570 | 0.70 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 120 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 83.4 Mpa |
| elongation | | ASTM D638 | 4.0 % |
| Flexural modulus | | ASTM D790 | 5880 Mpa |
| bending strength | | ASTM D790 | 127 Mpa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTM D257 | 1.0E+15 ohms·cm |
| dielectric strength | | ASTM D149 | 20 KV/mm |
| injection | Test Condition | Test Method | Test Result |
|---|
| drying temperature | | | 80 to 100 °C |
| drying time | | | 4.0 to 5.0 hr |
| Suggested maximum moisture content | | | < 0.20 % |
| Temperature at the rear of the barrel | | | 270 to 280 °C |
| Temperature in the middle of the barrel | | | 280 to 285 °C |
| Temperature at the front of the material cylinder | | | 285 to 290 °C |
| Spray nozzle temperature | | | 280 to 285 °C |
| Processing (melt) temperature | | | 280 to 285 °C |
| Temperature | | | 80 to 120 °C |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 235 °C |
| Heat distortion temperature | | ASTM D648 | 215 °C |
| melting temperature | | DSC | 260 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.