PBT+PET VALOX™ V8030CS resin
0
- Usages:Home appliance componentshandlesand covers
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792 | 1.43 g/cm³ | |
| ISO 1183 | 1.43 g/cm³ | ||
| Melt volume flow rate | ISO 1133 | 29.0 cm³/10min | |
| ISO 1133 | 75.0 cm³/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | Break | ISO 527-2/5 | 103 MPa |
| elongation | Yield | ASTM D638 | 2.7 % |
| Tensile strain | Yield | ISO 527-2/5 | 2.1 % |
| elongation | ASTM D638 | 8.6 % | |
| tensile strength | Break | ASTM D638 | 98.0 MPa |
| Tensile modulus | ASTM D638 | 6180 MPa | |
| ISO 527-2/1 | 5890 MPa | ||
| tensile strength | Yield | ASTM D638 | 99.0 MPa |
| Yield | ISO 527-2/5 | 95.0 MPa | |
| bending strength | ASTM D790 | 148 MPa | |
| Fracture bending strain | ISO 178 | 3.4 % | |
| elongation | ASTM D638 | 2.8 % | |
| Tensile strain | Break | ISO 527-2/5 | 2.0 % |
| Flexural modulus | ASTM D790 | 5580 MPa | |
| ISO 178 | 5480 MPa | ||
| bending strength | ISO 178 | 148 MPa | |
| ASTM D790 | 148 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256 | 58 J/m | |
| ISO 180/1A | 4.0 kJ/m² | ||
| ISO 180/1A | 4.1 kJ/m² | ||
| Charpy Notched Impact Strength | ISO 179/1eA | 24 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| vicat | ISO 306/A120 | 222 °C | |
| Hot deformation temperature (HDT) | ASTM D648 | 220 °C | |
| ASTM D648 | 173 °C | ||
| vicat | ASTM D15258 | 224 °C | |
| ISO 306/A50 | 222 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.