ABS Sinkral® B 732/E VERSALIS ITALY

Product Description

Certificates(0)

Datasheet

Product Description

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	-40°C	DIN 53453	NoBreak
Charpy Notched Impact Strength	23°C	DIN 53453	20	kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	28	kJ/m²
	Impact strength of cantilever beam gap	-40°C	ISO 180/1A	12	kJ/m²
		Impact strength of cantilever beam gap	23°C,3.20mm	ISO 180/4A	350	J/m
			Impact strength of cantilever beam gap	0°C,3.20mm	ISO 180/4A	300	J/m
				Impact strength of cantilever beam gap	-20°C,3.20mm	ISO 180/4A	200	J/m
				Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-40°C,3.20mm	ISO 180/4A	140	J/m
Impact strength of simply supported beam without notch	23°C	DIN 53453	NoBreak
flammability	Test Condition	Test Method	Test Result	Test Unit
Hot filament ignition temperature	3.0mm	IEC 60695-2-13	650	°C
UL flame retardant rating	1.5mm	Internal Method	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ASTM D790	45.0	MPa
Bending modulus		ASTM D790	2200	MPa
elongation	Break	ASTM D638	45	%
tensile strength		ASTM D638	44.0	MPa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature	--	ISO 306/B120	104	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/A120	109	°C
Hot deformation temperature	1.8MPa,Annealed	ASTM D648	100	°C
Linear coefficient of thermal expansion	MD	ASTM D696	9E-05	cm/cm/°C
thermal conductivity		ASTMC177	0.17	W/m/K
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	23°C,24hr	ASTM D570	0.30	%
Shrinkage rate		Internal Method	0.40to0.60	%
melt mass-flow rate	220°C/10.0kg	ISO 1133	4.5	g/10min
density		ISO 1183	1.04	g/cm³
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dissipation factor	1kHz	IEC 60250	0.015
Dielectric constant	1kHz	IEC 60250	3.10
Dielectric strength		IEC 60243-1	30	kV/mm
Surface resistivity		IEC 60093	1E+14	ohms
Volume resistivity		IEC 60093	1E+15	ohms·cm
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ISO 2039-2	103
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
Designation			ThermoplasticISO2580-ABS1.EG.105-04-35-20

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.