PBT 201-G30 202 FNA NANTONG ZHONGLAN

Form：Granules | Grade：Flame retardant enhanced grade

Properties:

Glass fiber reinforcedProcessabilityHigh rigidityFiller: Glass fiber reinf30% filler by weight

Typical Applications:

Electrical fieldElectronic fieldPlastic connectorsAutomotive sectorIndustrial machineryLighting applicationsElectrical/Electronic Applications

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Electrical field \| Electronic field \| Plastic connectors \| Automotive sector \| Industrial machinery \| Lighting applications \| Electrical/Electronic Applications
Properties:	Glass fiber reinforced \| Processability \| High rigidity \| Filler: Glass fiber reinf \| 30% filler by weight

Certificates

No Data...

Technical Data Sheet

other	Test Condition	Test Method	Test Result	Test Unit
characteristic			30%玻璃纤维增强.3.0mm阻燃 V-0.性能与长春4830相当
Color			本色
purpose			连接器.线圈骨架.散热风扇等
impact performance	Test Condition	Test Method	Test Result	Test Unit
Suspended wall beam without notch impact strength	23°C	ASTM D256	60.0	kJ/m²
machinability	Test Condition	Test Method	Test Result	Test Unit
Dry conditions			120-140℃ 3-4h
Processing temperature			220-250	°C
	Processing temperature			250-280	°C
	Processing temperature	Processing temperature			240-270	°C
Screw speed			<100	rpm
Mold temperature			60-80	°C
Melt Temperature			250-280	°C
pressure			6-18	Mpa
pressure	pressure			70-120	Mpa
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.8mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	1.6mm	UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ASTM D638	10500	Mpa
tensile strength	Break	ASTM D638	115	Mpa
Bending modulus		ASTM D790	8000	Mpa
bending strength		ASTM D790	180	Mpa
Impact strength of cantilever beam gap		ASTM D256/ISO 179	7.5	kg·cm/cm(J/M)ft·lb/in
tensile strength		ASTM D638/ISO 527	110	kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	8000	kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	180	kg/cm²(MPa)[Lb/in²]
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	220	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	208	°C
Combustibility (rate)		UL 94	V-0 3.0mm
Hot deformation temperature	HDT	ASTM D648/ISO 75	220	℃（℉）
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	250°C/2.16kg	ASTM D1238	16	g/10min
Shrinkage rate	MD	ASTM D955	0.40	%
Shrinkage rate	Shrinkage rate	TD	ASTM D955	0.60	%
Water absorption rate	Equilibrium,23°C,50%RH	ASTM D570	0.16	%
density		ASTM D792/ISO 1183	1.62
melt mass-flow rate		ASTM D1238/ISO 1133	15-25	g/10min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		ASTM D257	1.3E+16	ohms·cm
Dielectric strength		ASTM D149	20	KV/mm
Volume resistivity		ASTM D257/IEC 60093	1.3*10e16	Ω.cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.