Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.09 g/cm³ |
| Melt volume flow rate | | ISO1133 | 3.00 cm³/10min |
| Shrinkage rate | | ISO294-4 | 0.40到0.60 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO2039-2 | 100 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Bending stress | | ISO178 | 68.0 MPa |
| Tensile modulus | | ISO527-2 | 2000 MPa |
| Tensile stress | | ISO527-2 | 45.0 MPa |
| Flexural modulus | | ISO178 | 2100 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179 | 4.0 kJ/m² |
| Charpy Notched Impact Strength | | ISO179 | 12 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat Deflection Temperature | | ISO75-2/Af | 92.0 °C |
| Linear thermal expansion coefficient | | ISO11359-2 | 9E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare