PA6 H8202NLB

Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
Shrinkage rate		ASTMD955	1.3 %
Water absorption rate		ASTMD570	1.6 %
	Water absorption rate	Saturation	ASTMD570	9.5 %
	Water absorption rate	Water absorption rate	Equilibrium	ASTMD570	2.7 %
Extractable		内部方法	<0.8 %
water content		ASTMD6869	<0.10 %
Relative viscosity-@			2.61
		ASTMD789	46.0到52.0
density		ASTMD792	1.13 g/cm³
melt mass-flow rate		ASTMD1238	9.8 g/10min

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTMD785	119

Mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ASTMD638	2850 MPa
tensile strength		ASTMD638	79.0 MPa
elongation		ASTMD638	4.0 %
elongation	elongation		ASTMD638	55 %
Flexural modulus		ASTMD790	3010 MPa
bending strength		ASTMD790	110 MPa

Impact resistance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap		ASTMD256	50 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ASTMD256	60 J/m

Thermal performance	Test Method	Test Result
	ASTMD648	178 °C
		ASTMD648	65.0 °C
melting temperature	ASTMD3418	220 °C
	ASTME831	8.3E-05 cm/cm/°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.