Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 0.958 g/cm³ |
| melt mass-flow rate | | ISO 1133 | 0.45 g/10min |
| Environmental stress cracking resistance | | ASTM D1693 | >1000 hr |
| Carbon black content | | ASTM D1603 | 2.3 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ISO 868 | 64 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Break | ISO 527-2 | >30.0 MPa |
| Tensile strain | Break | ISO 527-2 | >600 % |
| aging | Test Condition | Test Method | Test Result |
|---|
| Retention of Mechanical Properties | | ISO 527 | >75 % |
| Retention of Mechanical Properties | | ISO 527 | >75 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric constant | | ASTM D1531 | 2.50 |
| Dissipation Factor | | ASTM D150 | 5E-03 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| brittle temperature | | ASTM D746 | -76.0 °C |
| vicat | | ISO 306/A | 125 °C |
| Oxygen induction time | | EN728 | >30 min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare