Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | g/cm³ | 1.23 -- |
| Shrinkage rate | | % | 0.65到0.80 -- |
| Water absorption rate | | % | 1.2 -- |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | | 122 107 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | | HB -- |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | MPa | 5500 3300 |
| tensile strength | | MPa | 110 70.0 |
| elongation | Break | % | 5.0 7.0 |
| Flexural modulus | | MPa | 5200 3300 |
| bending strength | | MPa | 175 90.0 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | J/m | 80 150 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ohms·cm | 1E+15 -- |
| dielectric strength | | kV/mm | 21 -- |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | °C | 170 -- |
| Continuous use temperature | | °C | 90.0到95.0 -- |
| | cm/cm/°C | 3E-05 -- |
| | °C | 185 -- |
| melting temperature | | °C | 214到220 -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.