PA+Olefin

PA+Olefin NEALID XG300 AD MAJORIS FRANCE

Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	-20°C	ISO 179/1eA	-- kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	41 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-20°C	ISO 179/1eU	-- kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	13 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.6mm	UL 94	HB
Burning wire flammability index	2.0mm	IEC 60695-2-12	650 °C

mechanical properties	Test Condition	Test Method	Test Result
bending strength		ISO 178	175 MPa
Bending modulus		ISO 178	7600 MPa
Tensile strain	Break	ISO 527-2	3.0 %
tensile strength	Break	ISO 527-2	180 MPa
Tensile modulus		ISO 527-2	8500 MPa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	MD	ISO 11359-2	2.7E-05 cm/cm/°C
Melting temperature		ISO 3146	220 °C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	186 °C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	200 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium,23°C,50%RH		1.0 %
Shrinkage rate			0.40to0.90 %
density		ISO 1183	1.28 g/cm³

Electrical performance	Test Condition	Test Method	Test Result
Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 0
Volume resistivity		DIN 53482	1E+15 ohms·cm
Surface resistivity		DIN 53482	1E+15 ohms

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.