Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | 内部方法 | 0.15到0.30 % |
| Water absorption rate | | ISO62 | 4.5 % |
| Water absorption rate | | ISO62 | 1.1 % |
| density | | ISO1183 | 1.41 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO2039-2 | 114 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| burning rate | | FMVSS302 | 2.0 mm/min |
| UL flame retardant rating | | UL94 | HB |
| UL flame retardant rating | | UL94 | HB |
| Burning wire flammability index | | IEC60695-2-12 | 650 °C |
| Hot filament ignition temperature | | IEC60695-2-13 | 650 °C |
| Limiting Oxygen Index | | ISO4589-2 | 27 % |
| burning rate | | FMVSS302 | 6.0 mm/min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2/1 | 10500 MPa |
| Tensile stress | Break | ISO527-2/5 | 180 MPa |
| Tensile strain | Break | ISO527-2/5 | 3.3 % |
| Flexural modulus | | ISO178 | 10000 MPa |
| Bending stress | | ISO178 | 280 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 10 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 60 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 80 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/1A | 9.0 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/1A | 10 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/1A | 11 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/1A | 12 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1eA | 9.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | IEC60243-1 | 19 kV/mm |
| | IEC60250 | 3.40 |
| | IEC60250 | 3.40 |
| | IEC60250 | 3.20 |
| Surface Resistivity | | IEC60093 | >1.0E+16 ohms |
| Volume resistivity | | IEC60093 | >1.0E+16 ohms·cm |
| Dissipation Factor | | IEC60250 | 6.8E-03 |
| Dissipation Factor | | IEC60250 | 6.8E-03 |
| Dissipation Factor | | IEC60250 | 0.015 |
| CTI | | IEC60112 | 500 V |
| CTI | | IEC60112 | 375 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| BallPressure Test | | IEC60695-10-2 | Pass |
| | ISO11359-2 | 2.2E-05 cm/cm/°C |
| | ISO11359-2 | 7.8E-05 cm/cm/°C |
| thermal conductivity | | ISO8302 | 0.33 W/m/K |
| RTI Elec | | UL746 | 65.0 °C |
| RTI Imp | | UL746 | 65.0 °C |
| RTI | | UL746 | 65.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare