POM F20-73R1 MITSUBISHI THAILAND

Form：Granules | Grade：Injection grade

Properties:

Weather resistanceMedium viscosity

Typical Applications:

Electronic and Electrical ApplicationsAutomotive sector

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Electronic and Electrical Applications \| Automotive sector
Properties:	Weather resistance \| Medium viscosity

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179	250	kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179	7.0	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.8mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ISO 178	91.0	Mpa
Bending modulus		ISO 178	2610	Mpa
Nominal tensile fracture strain		ISO 527-2	30	%
Tensile strain	Yield	ISO 527-2	8.5	%
tensile strength	Yield	ISO 527-2	65.0	Mpa
Tensile modulus		ISO 527-2	2900	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Melting temperature		ISO 11357-3	166	°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	100	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	160	°C
Linear coefficient of thermal expansion	TD	ISO 11359-2	1.1E-04	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD	ISO 11359-2	1.1E-04	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.22	%
Shrinkage rate	MD:3.00mm		2.0	%
Shrinkage rate	Shrinkage rate	TD:3.00mm		2.0	%
Melt Volume Flow Rate (MVR)	190°C/2.16kg	ISO 1133	7.90	cm3/10min
melt mass-flow rate	190°C/2.16kg	ISO 1133	9.1	g/10min
density		ISO 1183	1.41	g/cm³
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		IEC 60093	1E+14	ohms·cm
Surface resistivity		IEC 60093	1E+16	ohms

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.