ABS MG47 NA1000 SABIC INNOVATIVE MEXICO

Form：Granules | Grade：Injection grade

Properties:

Impact resistanceLow odorHigh mobilityCorrosion resistanceAcid and alkali resistantEasy to process and shape

Typical Applications:

Electrical componentsSpecial for outdoor products

Supplier(0)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Electrical components \| Special for outdoor products
Properties:	Impact resistance \| Low odor \| High mobility \| Corrosion resistance \| Acid and alkali resistant \| Easy to process and shape

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	9.0	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	26	kJ/m²
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	8.0	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	22	kJ/m²
Dart impact	23°C,TotalEnergy	ASTM D3763	30.0	J
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.5mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ASTM D638	2270	Mpa
Tensile modulus	Tensile modulus		ISO 527-2/1	2370	Mpa
tensile strength	Yield	ASTM D638	44.0	Mpa
	tensile strength	Yield	ISO 527-2/50	47.0	Mpa
		tensile strength	Break	ASTM D638	33.0	Mpa
		tensile strength	tensile strength	Break	ISO 527-2/50	35.0	Mpa
elongation	Yield	ASTM D638	2.0	%
Tensile strain	Yield	ISO 527-2/50	2.6	%
elongation	Break	ASTM D638	24	%
Tensile strain	Break	ISO 527-2/50	25	%
Bending modulus	50.0mmSpan	ASTM D790	2300	Mpa
Bending modulus	Bending modulus		ISO 178	2200	Mpa
bending strength		ISO 178	70.0	Mpa
bending strength	bending strength	Yield,50.0mmSpan	ASTM D790	70.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature	--	ISO 306/B50	98.0	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	100	°C
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	8.8E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	8.8E-05	cm/cm/°C
RTI Elec		UL 746	60.0	°C
RTI Imp		UL 746	60.0	°C
RTI Str		UL 746	60.0	°C
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	94.0	°C
	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	80.0	°C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	81.0	°C
Vicat softening temperature		ASTM D152510	99.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	230°C/3.8kg	ASTM D1238	5.6	g/10min
melt mass-flow rate	melt mass-flow rate	220°C/10.0kg	ISO 1133	18	g/10min
Shrinkage rate	MD：3.20mm	Internal Method	0.50-0.80	%
Melt viscosity	240°C,1000sec^-1	ASTM D3835	225	Pa·s
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
High voltage arc tracing rate	HVTR	UL 746	PLC 3
Hot wire ignition	HWI	UL 746	PLC 3
Arc resistance		ASTM D495	PLC6
Compared to the anti leakage trace index	CTI	UL 746	PLC 0
High arc combustion index	HAI	UL 746	PLC 0
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ASTM D785	112

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.