ASA/PC HRA222F-700653 SABIC INNOVATIVE US

Form：Granules | Grade：Injection grade

Properties:

High temperature resistanThermal stability

Typical Applications:

Home appliance componentsLawn garden equipment

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Home appliance components \| Lawn garden equipment
Properties:	High temperature resistan \| Thermal stability

Certificates

No Data...

Technical Data Sheet

flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	2.0 mm	UL 94	V-0
Extreme Oxygen Index		ISO 4589-2	29	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ISO 178	93.0	Mpa
Bending modulus		ISO 178	2510	Mpa
elongation	Break	ISO 527-2/5	> 50	%
	elongation	Break4	ASTM D638	> 100	%
		elongation	Break5	ASTM D638	> 100	%
			elongation	Yield	ISO 527-2/50	4.4	%
				elongation	Yield	ISO 527-2/5	4.3	%
					elongation	Yield4	ASTM D638	4.3	%
					elongation	elongation	Yield5	ASTM D638	4.2	%
tensile strength	Break	ISO 527-2/50	45.0	Mpa
	tensile strength	Break	ISO 527-2/5	51.0	Mpa
		tensile strength	Break4	ASTM D638	56.0	Mpa
			tensile strength	Break5	ASTM D638	66.0	Mpa
				tensile strength	Yield	ISO 527-2/50	60.0	Mpa
					tensile strength	Yield	ISO 527-2/5	62.0	Mpa
						tensile strength	Yield5	ASTM D638	59.0	Mpa
						tensile strength	tensile strength	Yield4	ASTM D638	63.0	Mpa
Tensile modulus	--	ISO 527-2/1	2520	Mpa
Tensile modulus	Tensile modulus	--3	ASTM D638	2590	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
Spray nozzle temperature			220 to 260	°C
Processing (melt) temperature			230 to 270	°C
Mold temperature			50 to 70	°C
drying temperature			80 to 90	°C
drying time			2.0 to 4.0	hr
Suggested maximum moisture content			0.020	%
Hopper temperature			60 to 80	°C
Temperature at the rear of the barrel			200 to 230	°C
Temperature in the middle of the barrel			220 to 260	°C
Temperature at the front of the material cylinder			230 to 270	°C
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm, 100 mm Span	ISO 75-2/Be	99.0	°C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 100 mm Span	ISO 75-2/Ae	88.0	°C
Vicat softening temperature	--	ISO 306/A50	111	°C
	Vicat softening temperature	--	ISO 306/B50	102	°C
	Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	104	°C
Ball Pressure Test	73 to 77°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	Flow : -30 to 80°C	ISO 11359-2	6.9E-5	cm/cm/°C
	Linear coefficient of thermal expansion	Across Flow : -30 to 80°C	ISO 11359-2	7.1E-5	cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : 23 to 80°C	ISO 11359-2	7.5E-5	cm/cm/°C
RTI Elec		UL 746	90.0	°C
RTI Imp		UL 746	90.0	°C
RTI		UL 746	90.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Outdoor applicability		UL 746C	f1
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.20	%
Water absorption rate	Water absorption rate	Saturation, 23°C	ISO 62	0.60	%
Shrinkage rate	Flow	Internal Method	0.40 - 0.60	%
Melt Volume Flow Rate (MVR)	260°C/2.16 kg	ISO 1133	13.0	cm3/10min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Compared to the anti leakage trace index		UL 746	PLC 0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.