Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.60 g/cm³ |
| Water absorption rate | | ISO 62 | 1.3 % |
| density | | ISO1183 | 1.60 g/cm³ |
| Water absorption rate | | ISO62 | 1.3 % |
| Moisture content | | ISO960 | <2000 ppm |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| UL flame retardant rating | | UL94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2/5 | 16000 MPa |
| Tensile stress | | ISO 527-2/5 | 210 MPa |
| Tensile strain | | ISO 527-2/5 | 2.5 % |
| Impact strength of cantilever beam gap | | ISO 180/1A | 13 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/1A | 15 kJ/m² |
| Tensile modulus | | ISO527-2/5 | 16000 MPa |
| Tensile stress | | ISO527-2/5 | 210 MPa |
| Tensile strain | | ISO527-2/5 | 2.5 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO180/1A | 13 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/1A | 15 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | 1E+13 ohms |
| Volume resistivity | | IEC 60093 | 1E+15 ohms·cm |
| CTI | | IEC 60112 | 500 V |
| Surface Resistivity | | IEC60093 | 1E+13 ohms |
| Volume resistivity | | IEC60093 | 1E+15 ohms·cm |
| CTI | | IEC60112 | 500 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat Deflection Temperature | | ISO 75-2/A | 250 °C |
| melting temperature | | ISO 11357 | 262 °C |
| Heat Deflection Temperature | | ISO 75-2/B | 260 °C |
| melting temperature | | ISO11357 | 262 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.