ABS Sinkral® PD L 322 VERSALIS ITALY

Product Description

Certificates(0)

Datasheet

Product Description

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	DIN 53453	无断裂
Impact strength of cantilever beam gap	-40°C,3.20mm	ISO 180/4A	50	J/m
	Impact strength of cantilever beam gap	-20°C,3.20mm	ISO 180/4A	70	J/m
		Impact strength of cantilever beam gap	0°C,3.20mm	ISO 180/4A	100	J/m
			Impact strength of cantilever beam gap	23°C,3.20mm	ISO 180/4A	170	J/m
				Impact strength of cantilever beam gap	-40°C4	ISO 180/1A	6.0	kJ/m²
				Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C4	ISO 180/1A	13	kJ/m²
Charpy Notched Impact Strength	23°C	DIN 53453	10	kJ/m²
Impact strength of simply supported beam without notch	-40°C	DIN 53453	无断裂
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.5mm	Internal Method	HB
Hot filament ignition temperature	3.0mm	IEC 60695-2-13	650	°C
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength		ASTM D638	45.0	MPa
elongation	Break	ASTM D638	20	%
Bending modulus		ASTM D790	2350	MPa
bending strength		ASTM D790	69.0	MPa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	MD	ASTM D696	9E-05	cm/cm/°C
thermal conductivity		ASTMC177	0.17	W/m/K
Hot deformation temperature	1.8MPa,Annealed	ASTM D648	96.0	°C
Vicat softening temperature	--	ISO 306/A120	99.0	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	96.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ISO 1183	1.04	g/cm³
melt mass-flow rate	220°C/10.0kg	ISO 1133	26	g/10min
Shrinkage rate		Internal Method	0.40to0.60	%
Water absorption rate	23°C,24hr	ASTM D570	0.30	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		IEC 60093	1E+14	ohms
Volume resistivity		IEC 60093	1E+15	ohms·cm
Dielectric strength		IEC 60243-1	30	kV/mm
Dielectric constant	1kHz	IEC 60250	3.10
Dissipation factor	1kHz	IEC 60250	0.015
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Sale	ISO 2039-2	109

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.