PA66 A 246 M SOLVAY FRANCE

Form：Granules | Grade：Toughened grade

Typical Applications:

Application in the automotive fieldsporting goods

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:

Application in the automotive field | sporting goods

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	16	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak
Charpy Notched Impact Strength	23°C	ISO 179/1eA	97	kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180	60	kJ/m²
	Impact strength of cantilever beam gap	-30°C	ISO 180	22	kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ASTM D256	100	J/m
flammability	Test Condition	Test Method	Test Result	Test Unit
Extreme Oxygen Index		ISO 4589-2	25	%
UL flame retardant rating	1.6mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	23°C	ISO 178	70.0	Mpa
bending strength	bending strength	23°C	ASTM D790	70.0	Mpa
Bending modulus	23°C	ISO 178	1800	Mpa
Bending modulus	Bending modulus	23°C	ASTM D790	1800	Mpa
elongation	Break,23°C	ASTM D638	80	%
Tensile strain	Yield,23°C	ISO 527-2	20	%
tensile strength	Break,23°C	ISO 527-2/1A	44.0	Mpa
	tensile strength	Yield,23°C	ISO 527-2/1A	47.0	Mpa
	tensile strength	tensile strength	Yield,23°C	ASTM D638	50.0	Mpa
Tensile modulus	23°C	ISO 527-2/1A	1900	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Melting temperature		ISO 11357-3	263	°C
Melting temperature	Melting temperature		ASTM D3417	263	°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/Af	65.0	°C
	Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	63.0	°C
	Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	200	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	23°C,24hr	ISO 62	1.1	%
density		ISO 1183/A	1.08	g/cm³
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		IEC 60093	1E+15	ohms·cm
Surface resistivity		IEC 60093	1E+15	ohms
Dielectric strength	2.00mm	IEC 60243-1	30	KV/mm
Relative permittivity		IEC 60250	3.20
Dissipation factor		IEC 60250	0.020
Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 1
Compared to the anti leakage trace index	Compared to the anti leakage trace index	SolutionB	IEC 60112	PLC 1

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.