Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.80 g/cm³ |
| Shrinkage rate | | ISO 294-4 | 0.050 % |
| Water absorption rate | | ISO 62 | 0.50 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Limiting Oxygen Index | | ISO 4589-2 | 22 % |
| UL flame retardant rating | | UL 94 | HB |
| Hot filament ignition temperature | | IEC 60695-2-13 | 750 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | Compression Molded | ISO 178 | 10000 MPa |
| bending strength | Compression Molded | ISO 178 | 180 MPa |
| Tensile modulus | Compression Molded | ISO 527-2 | 12000 MPa |
| tensile strength | | ISO 527-2 | 75.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | Compression Molded | ISO 179 | 80 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | 1E+12 ohms |
| Volume resistivity | | IEC 60093 | 1E+15 ohms·cm |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Glass Transition Temperature | | DSC | 130 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 1.2E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.